EPOXY HARDENER

Adduct Hardener, Solvent-based

Epoxy resin adducted polyaminoamides. High chemical resistance, fast physical drying, good adhesion.

MERGINAMID A 112

Merginamid A 112 is a modified polyaminoamide adduct containing solvents (xylene/ n-butanol) which, in combination with solutions of solid epoxy resins, leads to tack-free film formation even at high humidity and temperatures of around ten degrees Celsius.

Download Datasheet

Produktname

MERGINAMID A 112

Aminzahl

130-145 mg KOH/g

Funktion

Korrosionsschutz, LH-haltige Beschichtungen, klebfreie Folien auch bei 80 % relativer Luftfeuchtigkeit

H-aktiv-Ă„quivalent

520 g/Eq

Viskosität

1.400 – 2.200 mPa*s bei 20 °C

Biobasierter Kohlenstoffanteil

38 %

MERGINAMID A 130

Merginamid A 130 is a modified polyaminoamide adduct containing solvents (xylene/n-butanol) which, in combination with solutions of solid epoxy resins, leads to tack-free film formation even at high humidity and temperatures of around ten degrees Celsius. It is the accelerated version of the A 112.

Download Datasheet

Product name

MERGINAMID A 130

Amine value

145 – 165 mg KOH/g

Function

Corrosion protection, as with A 112, but also at temperatures around 5 ° C

H-active equivalent

520 g/Eq

Viscosity

1.400 – 2.200 mPa*s at 20 °C

Biobased carbon content

43 %

MERGINAMID A 140

Merginamide A 140 is a solvent-containing (xylene /; N-butanol) polyaminoamide adduct hardener which, in combination with solutions of solid epoxy resins having an epoxy equivalent weight of approx. 475, is suitable for the formulation of cold-curing solvent-containing coatings for use in corrosion protection on steel (eg shipbuilding) and mineral substrates (eg in construction).

Download Datasheet

Product name

MERGINAMID A 140

Amine value

140-160 mg KOH/g

Function

Corrosion protection, shipbuilding, mineral substrates

H-active equivalent

340 g/Eq

Viscosity

7.000 – 9.000 mPa*s at 25 °C

Biobased carbon content

50 %