Showing 1–12 of 27 results
Isomergic acid SF is a very light conjugated fatty acid with very good color stability. It is suitable for alkyd and polyester resins, in particular for vinylated and acrylated systems, with which they can copolymerize according to the Diels-Alder mechanism.
| Product name | ISOMERGINSÄURE SF |
|---|---|
| C 18:2 conjugated | 55 – 60 % |
| Acid number | 198 – 202 mg KOH / g |
| Iodine Value | 130 – 150 gI₂ / 100 g |
| Biobased carbon content | 100 % |
| Product name | ISOMERGIC ACID SY |
|---|---|
| C 18:2 conjugated | 50 – 55 [%] |
| Acid number | 198 – 202 [mg KOH / g] |
| Iodine Value | 125 – 140 [g I₂ / 100 g] |
| Biobased carbon content | 100 [%] |
| Product name | MERGINAMID A 112 |
|---|---|
| Amine value | 130-145 mg KOH/g |
| Function | Corrosion protection, LH-containing coatings, adhesive-free films even at 80% relative humidity |
| H-active equivalent | 520 g/Eq |
| Viscosity | 1.400 – 2.200 mPa*s at 20 °C |
| Biobased carbon content | 38 % |
| Product name | MERGINAMID A 130 |
|---|---|
| Amine value | 145 – 165 mg KOH/g |
| Function | Corrosion protection, as with A 112, but also at temperatures around 5 ° C |
| H-active equivalent | 520 g/Eq |
| Viscosity | 1.400 – 2.200 mPa*s at 20 °C |
| Biobased carbon content | 43 % |
| Product name | MERGINAMID A 140 |
|---|---|
| Amine value | 140-160 mg KOH/g |
| Function | Corrosion protection, shipbuilding, mineral substrates |
| H-active equivalent | 340 g/Eq |
| Viscosity | 7.000 – 9.000 mPa*s at 25 °C |
| Biobased carbon content | 50 % |
| Product name | MERGINAMID A 154 |
|---|---|
| Viscosity | 18.000 – 30.000 mPa*s at 25 °C |
| Amine value | 105 – 125 mg KOH/g |
| Function | Corrosion protection, surface treatment |
| H-active equivalent | 260 g/Eq |
| Solid content | 39-41 % |
| Biobased carbon content | 34 % |
| Product name | MERGINAMID A 155/2 |
|---|---|
| Viscosity | 13.000 – 23.000 mPa*s at 25 °C |
| Amine value | 155 – 175 mg KOH/g |
| Function | Corrosion protection, surface treatment |
| H-active equivalent | 210 g/Eq |
| Solid content | 49 – 51 % |
| Biobased carbon content | 34 % |
| Product name | MERGINAMID A 160 |
|---|---|
| Viscosity | 30.000 – 50.000 mPa*s at 25 °C |
| Amine value | 135 – 155 mg KOH/g |
| Function | Corrosion protection, surface treatment |
| H-active equivalent | 210 g/Eq |
| Solid content | 49 – 51 % |
| Biobased carbon content | 34 % |
| Product name | MERGINAMID A 210/5 |
|---|---|
| Viscosity | 18.000 – 28.000 mPa*s at 25 °C |
| Amine value | 170 – 200 mg KOH/g |
| Function | Corrosion protection, surface treatment |
| H-active equivalent | 230 g/Eq |
| Solid content | 54 – 56 % |
| Biobased carbon content | 0 % |
| Product name | MERGINAMID A 260 |
|---|---|
| Viscosity | 8.000 – 12.000 mPa*s bei 40 °C |
| Amine value | 265 – 295 mg KOH/g |
| Function | Corrosion protection, surface treatment |
| H-active equivalent | 170 g/Eq |
| Solid content | 100 % |
| Biobased carbon content | 59 % |
| Product name | MERGINAMID A 280 |
|---|---|
| Viscosity | 1.000 – 2.000 mPa*s at 25 °C |
| Amine value | 250 – 290 mg KOH/g |
| Function | Corrosion protection, surface treatment |
| H-active equivalent | 115 g/Eq |
| Solid content | 100 % |
| Biobased carbon content | 40 % |
| Product name | MERGINAMID L 190/70 |
|---|---|
| Viscosity | 440 – 1.250 mPa*s at 25 °C |
| Amine value | 155 – 185 mg KOH/g |
| Function | Corrosion protection, direct to metal, surface protection of wood, concrete and plastics, adhesives. High chemical resistance, very good adhesion. |
| H-active equivalent | 340 g/Eq |
| Solid content | 69 – 71 % |